realloy C
- With a special composition
- Excellent bonding with ceramics
- Can be melted with all casting methods
- Easy finishing and easy to polish after casting
- Also suitable for laser welding
- Easy oxide removel after the ceramic firing
- Does not dust when milling
- Worldwide proven quality
- Best in its class
- Biocompatible
Casting Ingot
Composition
Co 62,5 % | Cr 24,6 % | W 8,5 % | Mo 2,9 % | Si 1,3 % |
Nb, Mn, Fe, N < 1,0 %
This alloy is Nickel and Beryllium free and complies EN ISO 22674, Typ 4
Proberties
Density 8,3 g/cm³
Vickers hardness 285 (HV10)
Linear CTE (25 - 500 °C) 13,9 (10-6·K-1)
Linear CTE (25 - 600 °C) 14,0 (10-6·K-1)
Melting interval 1304 - 1369 (°C)
Casting temperature 1470 (°C)
Recommended burning temperatur 980 (°C)
Proof strength (Rp 0,2) 490 (MPa)
Tensile strength (Rm) 920 (MPa)
Modulus of elasticity 210 (GPa)
Tensile elongation (A5) 10 (%)
Co 62,5 % | Cr 24,6 % | W 8,5 % | Mo 2,9 % | Si 1,3 % |
Nb, Mn, Fe, N < 1,0 %
This alloy is Nickel and Beryllium free and complies EN ISO 22674, Typ 4
Proberties
Density 8,3 g/cm³
Vickers hardness 285 (HV10)
Linear CTE (25 - 500 °C) 13,9 (10-6·K-1)
Linear CTE (25 - 600 °C) 14,0 (10-6·K-1)
Melting interval 1304 - 1369 (°C)
Casting temperature 1470 (°C)
Recommended burning temperatur 980 (°C)
Proof strength (Rp 0,2) 490 (MPa)
Tensile strength (Rm) 920 (MPa)
Modulus of elasticity 210 (GPa)
Tensile elongation (A5) 10 (%)
CAD/CAM
Softblank
Powder 15-45 μm
Powder 10-30 μm