realloy CH
- High stability
- Can be melted with all casting methods
- Tested and proven alloy for many years
- Biocompatible
Casting Ingot
Composition
Co 63,0 % | Cr 29,0 % | Mo 5,8 % | Si 1,2 % | Fe, Mn, Nb < 1,0 %
This alloy is Nickel and Beryllium free and complies with in EN ISO 22674, Typ4
Proberties
Density 8,2 g/cm³
Vickers hardness 330 (HV10)
Linear CTE (25 - 500 °C) 14,2 (10-6·K-1)
Linear CTE (25 - 600 °C) 14,4 (10-6·K-1)
Melting interval 1290 - 1370 (°C)
Casting temperature 1470 (°C)
Recommended burning temperatur 980 (°C)
Proof strength (Rp 0,2) 610 (MPa)
Modulus of elasticity 200 (GPa)
Tensile elongation (A5) 6,5 (%)
Tensile strength (Rm) 610 (MPa)
Co 63,0 % | Cr 29,0 % | Mo 5,8 % | Si 1,2 % | Fe, Mn, Nb < 1,0 %
This alloy is Nickel and Beryllium free and complies with in EN ISO 22674, Typ4
Proberties
Density 8,2 g/cm³
Vickers hardness 330 (HV10)
Linear CTE (25 - 500 °C) 14,2 (10-6·K-1)
Linear CTE (25 - 600 °C) 14,4 (10-6·K-1)
Melting interval 1290 - 1370 (°C)
Casting temperature 1470 (°C)
Recommended burning temperatur 980 (°C)
Proof strength (Rp 0,2) 610 (MPa)
Modulus of elasticity 200 (GPa)
Tensile elongation (A5) 6,5 (%)
Tensile strength (Rm) 610 (MPa)
CAD/CAM